Investigation of the Thermo Barrier Coatings of the Y–Al–O System Using Synchrotron Radiation

A. Yu. Nazarov; Назаров А. Ю.; E. L. Vardanyan; Варданян Э. Л.; A. A. Maslov; Маслов А. А.; A. A. Nikolaev; Николаев А. А.; K. N. Ramazanov; Рамазанов К. Н.; A. M. Khusainova; Хусаинова А. М.; A. N. Shmakov; Шмаков А. Н.

doi:10.31857/S1028096023040155

Investigation of the Thermo Barrier Coatings of the Y–Al–O System Using Synchrotron Radiation

作者: Nazarov A.Y.¹, Vardanyan E.L.¹, Maslov A.A.¹, Nikolaev A.A.¹, Ramazanov K.N.¹, Khusainova A.M.¹, Shmakov A.N.²
隶属关系:
1. Ufa State Aviation Technical University
2. Budker Institute of Nuclear Physics of Siberian Branch RAS
期: 编号 4 (2023)
页面: 25-29
栏目: Articles
URL: https://ruspoj.com/1028-0960/article/view/664574
DOI: https://doi.org/10.31857/S1028096023040155
EDN: https://elibrary.ru/JRUDAN
ID: 664574

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅或者付费存取

详细
作者简介
参考
补充文件
统计

详细

Y–Al–O thermal barrier coating was investigated using synchrotron radiation. Y–Al–O coating was deposited on molybdenum substrate using cathodic-arc deposition with two elemental cathodes made from aluminum and yttrium respectively. Phase evolution was investigated during samples heating up to 1500°C in vacuum. It was found that as-deposited coating has amorphous structure and crystallization process take place at 1160–1170°C, no another phase transformations was observed. Qualitative phase composition of coating as well as microstresses in film were determined. The results of evaluation demonstrates lack of microstresses in obtained coating. Obtained results demonstrates a possibility of Y–Al–O coating deposition by cathodic arc deposition Arc-PVD technology, and deposited coating consist of YAlO₃ (predominantly), Y₂O₃ oxides and YAl₂ intermetallic.

关键词

plasma treatment, vacuum arc deposition, thermal barrier coating, synchrotron radiation, X-ray diffraction analysis, microstress.

参考

Riallant F., Cormier J., Longuet A. // Metall. Mater. Trans. A. 2014. V. 45. P. 351. https://www.doi.org/10.1007/s11661-013-1961-y
Kunal M., Luis N., Calvin M.D. // Industrial & Engineering Chem. Res. 2021. V. 60. № 17. P. 6061. https://www.doi.org/10.1021/acs.iecr.1c00788
Zhang C., Lv P., Xia H., Yang Z., Konovalov S. // Vacuum. 2019. V. 167. P. 263. https://www.doi.org/10.1016/j.vacuum.2019.06.022
Alymov M.I., Stolin A.M., Bazhin P.M. // Industrial Laboratory. Materials Diagnostics. 2022. V. 88. № 2. P. 40. https://www.doi.org/10.26896/1028-6861-2022-88-2-40-48
Bin L, Yuchen L, Changhua Z. // J. Mater. Sci. Technol. 2019. V. 35. № 5. P 833. https://www.doi.org/10.1016/j.jmst.2018.11.016
Yoo Y.S. // Korean J. Chem. Eng. 2014. V. 17. P. 1.
Vaßen R., Jarligo M.O., Steinke T., Mack D. E., Stöver D. // Surf. Coat. Technol. 2010. V. 205. № 4. P. 938. https://www.doi.org/10.1016/j.surfcoat.2010.08.151
Uwe S. // Aerospace Sci. Technol. 2003. V. 7. № 1. P. 73. https://www.doi.org/10.1016/S1270-9638(02)00003-2
Clarke D., Oechsner M., Padture N. // MRS Bulletin. 2012. V. 37. № 10. P. 891. https://www.doi.org/10.1557/mrs.2012.232
Padture N. // Nature Mater. 2016. V. 15. P. 804. https://www.doi.org/10.1038/nmat4687
Cao X.Q., Vassen R., Stoever D. // J. Europ. Ceram. Soc. 2004. V. 24. № 1. P. 1. https://www.doi.org/10.1016/S0955-2219(03)00129-8
Мубояджян С.А. , Будиновский С.А., Гаямов А.М., Матвеев П.В. // Авиационные материалы и технологии. 2013. № 1. С. 17.
Bacos M.-P., Dorvaux J.-M., Lavigne O. et al. // Aerospace Lab. 2011. Iss. 3. P. AL03-03.
Shi M., Xue Zh., Zhang Zh. et al. // Surf. Coat. Technol. 2020. V. 395. P. 125913. https://www.doi.org/10.1016/j.surfcoat.2020.125913
Zhan X., Li Zhen, Liu B. et al. // J. Am. Ceram. Soc. 2012. V. 95. № 4. P. 1429. https://www.doi.org/10.1111/j.1551-2916.2012.05118.x
Xin Z., Zhenhua X., Xizhi F. // Mater. Lett. 2014. V. 134. P. 146. https://www.doi.org/10.1016/j.matlet.2014.07.027
Lu Z. et al. // Materials Today: Proceedings. 2014. V. 1. № 1. P. 35. https://www.doi.org/10.1016/j.matpr.2014.09.009.
Zhou X., Xu Zh., Fan X. et al. // Mater. Lett. 2014. V. 134. P. 146. https://www.doi.org/10.1016/j.matlet.2014.07.027